Polyacrylamide flocculating agent has been used in the Leaching Division 'of the Risdon Works of the Electrolytic Zinc Company of Australasia Limited since October, 1960. The number of thickeners in the continuous thickening stage was thereby reduced from eight to three. There has been an increase of 25 per cent in throughput and a reduction of solids in thickener over-flow from 3-4 g/l. solids to 05 g Ir. solids. Reagent addition has been at the rate of 025 lb Separan NP10 per ton solids.Additionally there has been a gain of 3 per cent in current efficiency as the direct result of the addition of Separan NP10 to purified cadmium sulphate solution priOl; to electrolysis for cadmium metal. A smoother deposit has resulted and it has been possible to increase deposition time between strippings from 47 to 71 hr. However, there has been a slight increase in the lead content of the cadmium metal produced.The use of Separan NP10 to settle copper bearing residue in a batch process stage has resulted in a five-fold increase in settlement rate and a reduction in purification cycle time.INTRODUCTIONThe Electrolytic Zinc Company of Australasia Limited, Risdon, Tasmania, produces zinc by electrolysis of purified zinc sulphate solution, the raw material being zinc sulphide concentrate. In the Risdon process (Van Arsdale, 1953; J ohnstone, 1953; Ross, 1949) the compound zinc ferrite (ZnO.Fe203) is formed during the concentrate roasting stage. When the roasted material is leached in dilute sulphuric acid the zinc ferrite is not attacked, and it remains as part of the insoluble leach residue, of which it may form as much as two-thirds of the whole. The remainder is mainly unroasted zinc sulphide, unleached zinc oxide, lead sulphate, gypsum, silver compounds etc. The zinc in the residue may be 10 per cent of that in the original concentrate.Continuous thickeners are used to recover the valuable residue from the impure zinc sulphate solution and the...